Effects of Sm3+/PMAA on mechanical and thermal properties of natural rubber latex film

文献类型： 外文期刊

第一作者： Zhang, Li

作者： Zhang, Li;Chen, Jing;Ma, Lin;Huang, Qianqian;Ju, Guoxian;Chen, Meilian;Liao, Lusheng;Zhang, Fuquan

作者机构：

关键词： natural rubber latex; PMAA; properties; Sm3+

期刊名称：POLYMER ENGINEERING AND SCIENCE （ 影响因子：2.428； 五年影响因子：2.276 ）

ISSN： 0032-3888

年卷期： 2021 年 61 卷 5 期

页码：

收录情况： SCI

摘要： Samarium carbonate [Sm-2(CO3)(3)] was taken as the source of Sm3+, and methyl acrylic acid (MAA) was employed as the precursor to prepare polymethacrylic acid (PMAA). The mixture of Sm-2(CO3)(3) and PMAA was marked as "SmP." The SmP prepared under different conditions was added to natural rubber (NR) latex to prepare NR/SmP films. The influence of the polymerization temperature of MAA and the amount of SmP on the mechanical properties and structure of NR/SmP films were analyzed. The results show that polymerization temperature has significant effect on the mechanical properties of NR/SmP film; lower temperature is benefit to improve modulus and rigidity, whereas higher temperature helps maintain good elasticity. Compared with neat NR, addition of 5-phr Sm-2(CO3)(3) results in a 30%-37% increase of tensile strength. Furthermore, the glass transition temperature (T-g) can also be increased by the addition of SmP; and the tan delta curves of all samples exhibit only one transition peak and indicate no phase separation between SmP and NR matrix. The influence of SmP on the structure and morphology of NR was explored by Fourier transform infrared, X-ray diffraction, thermogravimetric analysis, and scanning electron microscopy analysis; and the results show that SmP can be dispersed uniformly in the NR latex when loading of Sm-2(CO3)(3) is lower than 20 phr.

分类号：

  • 相关文献
作者其他论文 更多>>

微信小程序