Nitrogen-doped porous carbon derived from chitosan for the enhanced dehydrochlorination of lindane under mild conditions

文献类型： 外文期刊

第一作者： Yang, Jirui

作者： Yang, Jirui;Shen, Feng;Qiu, Mo;Qi, Xinhua

作者机构：

关键词： Lindane; Dechlorination; Dehydrochlorination; Chitosan; Nitrogen-doped porous carbon; Solid base

期刊名称：ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH （ 影响因子：4.223； 五年影响因子：4.306 ）

ISSN： 0944-1344

年卷期： 2018 年 25 卷 35 期

页码：

收录情况： SCI

摘要： Dehydrochlorination of lindane is commonly conducted in homogeneous alkaline solutions, possessing a series of problems such as corrosion and poor recyclability. In order to overcome the pervasive problems concerning homogeneous catalysts, heterogeneous catalysts have been increasingly employed in the applications. In this study, nitrogen-doped porous carbons (NPCs) were developed by a simple way in which chitosan and ZnCl2 were employed as the precursor and activation agent, respectively. NPCs exhibited high surface area (1111-1497 m(2)/g) and large porosity (0.464-0.621 cm(3)/g), resulting in a great adsorption affinity to lindane and the by-products. As solid bases, NPCs displayed an enhanced catalytic activity on lindane dehydrochlorination. This was closely related to the amount of pyridinic nitrogen on the pore surface, which could be tuned by the synthesis temperature. The optimal removal efficiency of lindane was up to 99.9% in presence of A800 (a NPC catalyst) at moderate pH (9.0) and mild temperature (45 degrees C) after incubation for 24 h. The rate constant for A800 suspension was improved by 2-3 orders of magnitude in comparison with that obtained in homogeneous solution at moderate pH (9.0) and mild temperatures (25-45 degrees C). The reusability of the material was evaluated by cycling for three times without noticeably reduced catalytic activity. This study provides a novel strategy to achieve partial dechlorination of chlorinated organic pollutants.

分类号：

  • 相关文献
作者其他论文 更多>>

微信小程序