Preparation and characterization of a novel fluoro-silicone acrylate copolymer by semi-continuous emulsion polymerization

文献类型： 外文期刊

第一作者： Xu, Lin

作者： Xu, Lin;Dai, Wei-shuai;Xie, Hong-de;Xu, Lei;Tsuboi, Taiju

作者机构：

关键词： Fluoro-silicone copolymer;Nano-particle;Emulsion polymerization;Hydrophobic

期刊名称：JOURNAL OF FLUORINE CHEMISTRY （ 影响因子：2.05； 五年影响因子：2.019 ）

ISSN：

年卷期：

页码：

收录情况： SCI

摘要： A novel fluoro-silicone acrylate (FSA) copolymer latex was synthesized with 2-acrylamido-2-methyl-propanesulfonic acid (AMPS), which served as a polymerizable emulsifier by semi-continuous emulsion polymerization. Methyl methacrylate (MMA), butyl acrylate (BA) and 1,3,5-trimethyltris (3,3,3-trifluoropyropyl) cyclotrisiloxane (D3F) were served as co-monomers while vinyltriethoxysilane (VTES) was used as a cross-linking agent. The structure and surface morphologies of the copolymer were characterized by FT-IR, 'H NMR, TEM, TGA and DSC. The influences of AMPS, D3F and VTES on the copolymer's properties of appearance, conversion rate, gel rate and solid content were discussed. The analytical results indicated that the FSA copolymer latex had a narrow particle size distribution around 100 nm with high temperature stability. The copolymer latex shows excellent water repellency with the contact angles of cotton and silk textile of 125.8° and 120.7°, respectively.

分类号： O6

  • 相关文献

[1]Synthesis and Characterization of Polysiloxane and Acrylate Elastomer Material. Xu, Lei,Wang, Min,Jiang, Xi-Zhi,Zhao, Yong-Fu. 2015

[2]Effect of ethyleneglycol dimethacrylate crosslinker on the performance of core-double shell structure poly(vinyl acetate-butyl acrylate) emulsion. Li Gang,Wang Ting,Fu Xin,Li Gang,Wang Ting,Huang Maofang,Gao Tianming. 2015

[3]Ultrasonically initiated emulsion polymerization of methyl methacrylate. Liao, YQ,Wang, Q,Xia, HS,Xu, X,Baxter, SM,Slone, RV,Wu, SG,Swift, G,Westmoreland, DG. 2001

[4]Ultrasonically initiated emulsion polymerization of n-butyl acrylate. Wang, Q,Xia, HS,Liao, YQ,Xu, X,Baxter, SM,Slone, RV,Wu, SG,Swift, G,Westmoreland, DG.

作者其他论文 更多>>

微信小程序