Evolution of the microstructure and mechanisms of performance degradation in EB-PVD YSZ thermal barrier coatings corroded by volcanic ash at 1150 degrees C

文献类型： 外文期刊

第一作者： Xia, J.

作者： Xia, J.;Xia, J.;Zhang, L.;Matsushita, Y.;Wu, R. T.

作者机构：

关键词： Ceramic; Molten salts; SEM; TEM; X-ray diffraction; High temperature corrosion

期刊名称：CORROSION SCIENCE （ 影响因子：7.72； 五年影响因子：8.104 ）

ISSN： 0010-938X

年卷期： 2022 年 208 卷

页码：

收录情况： SCI

摘要： Volcanic ash (VA)/calcium-magnesium-alumina-silicate (CMAS) corrosion is a crucial issue causing the failure of thermal barrier coatings. This study focuses on the degradation process of electron-beam physical vapor deposition yttria-stabilized zirconia by natural VA at 1150 degrees C. The phase transformation and chemical reaction during VA attack were measured in real-time by in-situ high-temperature X-ray diffraction. The mechanical properties and the thermal conductivity of the as-deposited and VA corroded coatings were investigated. The correlation between these microstructural changes and the coatings' properties are discussed. The degradation mechanisms are expected to guide the development of potential VA/CMAS mitigation methods.

分类号：

  • 相关文献
作者其他论文 更多>>

微信小程序