Ultrasonically initiated emulsion polymerization of n-butyl acrylate

文献类型： 外文期刊

第一作者： Wang, Q

作者： Wang, Q;Xia, HS;Liao, YQ;Xu, X;Baxter, SM;Slone, RV;Wu, SG;Swift, G;Westmoreland, DG

作者机构：

关键词： ltrasonic irradiation;emulsion polymerization;n-butyl acrylate

期刊名称：POLYMER INTERNATIONAL （ 影响因子：2.99； 五年影响因子：2.74 ）

ISSN：

年卷期：

页码：

收录情况： SCI

摘要： Ultrasonically initiated emulsion polymerization of n-butyl acrylate (BA) without added initiator has been studied. The experimental results show that high conversion of BA can be reached in a short time by employing an ultrasonic irradiation technique with a high purge rate of N_2. The viscosity average molecualr weight of poly(n-butyl acrylate) (PBA) obtained reaches 5.24 x 10~6 g mol~(-1). The ultrasonically initiated emulsion polymerization is dynamic and complicated, with polymerization of monomer and degradation of polymer occurring simultaneously. An increase in ultrasound intensity leads to an increase in polymerization rate in the range of cavitation threshold and cavitation peak values. Lower monomer concentration favours enhancement of the polymerization rate. ~1H NMR, ~(13)C NMR and FTIR spectroscopies reveal that there are some branches and slight crosslinking, and also carboxyl groups in PBA. Ultrasonically initiated emulsion polymerizaiton offers a new route for the preparation of nanosized latex particles; the particle size of PBA prepared is around 50-200 nm as measured by transmission electron microscopy.

分类号： O63`TQ31

  • 相关文献

[1]Polymerization rate and mechanism of ultrasonically initiated emulsion polymerization of n-butyl acrylate. Xia, HS,Wang, Q,Liao, YQ,Xu, X,Baxter, SM,Slone, RV,Wu, SG,Swift, G,Westmoreland, DG. 2002

[2]Synthesis and Characterization of Polysiloxane and Acrylate Elastomer Material. Xu, Lei,Wang, Min,Jiang, Xi-Zhi,Zhao, Yong-Fu. 2015

[3]Effect of ethyleneglycol dimethacrylate crosslinker on the performance of core-double shell structure poly(vinyl acetate-butyl acrylate) emulsion. Li Gang,Wang Ting,Fu Xin,Li Gang,Wang Ting,Huang Maofang,Gao Tianming. 2015

[4]Ultrasonically initiated emulsion polymerization of methyl methacrylate. Liao, YQ,Wang, Q,Xia, HS,Xu, X,Baxter, SM,Slone, RV,Wu, SG,Swift, G,Westmoreland, DG. 2001

[5]Preparation and characterization of a novel fluoro-silicone acrylate copolymer by semi-continuous emulsion polymerization. Xu, Lin,Dai, Wei-shuai,Xie, Hong-de,Xu, Lei,Tsuboi, Taiju.

作者其他论文 更多>>

微信小程序