Synthesis and Characterization of Wooden Magnetic Activated Carbon Fibers with Hierarchical Pore Structures

文献类型： 外文期刊

第一作者： Li, Dongna

作者： Li, Dongna;Li, Jianing;Li, Tongtong;Li, Dongna;Ren, Biyun;Ma, Xiaojun

作者机构：

关键词： magnetic iron oxide nanoparticles; wooden activated carbon fiber; biocompatible; adsorption; magnetic properties

期刊名称：POLYMERS （ 影响因子：4.329； 五年影响因子：4.493 ）

ISSN： 2073-4360

年卷期： 2018 年 10 卷 4 期

页码：

收录情况： SCI

摘要： Wooden magnetic activated carbon fibers (WMACFs) with hierarchical pore structures were obtained by adding magnetic iron oxide (Fe3O4) nanoparticles into the liquefied wood. The structures and properties of WMACFs were analyzed by scanning electronmicroscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), N-2 adsorption, and vibrating sample magnetometer (VSM). The results showed that WMACFs had high Brunauer-Emmett-Teller (BET) surface area (1578 m(2)/g) and total pore volume (0.929 cm(3)/g), of which 45% was the contribution of small mesopores of 2-3 nm. It is believed that Fe3O4 nanoparticles play an important role in the formation of hierarchical pores. With the Fe3O4 content increasing, the yield rate of WMACFs decreased, and the Fe3O4 crystal plane diffraction peaks and characteristic adsorption peaks were obviously observed. At the same time, it was also found that WMACFs had favorable magnetic properties when the Fe3O4 content was above 1.5%. As a result, WMACFs could be a promising candidate for high efficiency, low cost, and convenient separation for the magnetic field.

分类号：

  • 相关文献
作者其他论文 更多>>

微信小程序